Registration Dossier

Diss Factsheets

Physical & Chemical properties

Viscosity

Currently viewing:

Administrative data

Link to relevant study record(s)

Reference
Endpoint:
viscosity
Type of information:
experimental study
Adequacy of study:
key study
Study period:
2006-01-04 to 2006-01-26
Reliability:
1 (reliable without restriction)
Rationale for reliability incl. deficiencies:
guideline study
Qualifier:
according to guideline
Guideline:
OECD Test Guideline 114 (Viscosity of Liquids)
Qualifier:
according to guideline
Guideline:
DIN 51562 Part 1 (Viscometry - Measurement of kinematic viscosity by means of the Ubbelohde viscometer - Part 1: Viscometer specification and measurement procedure)
GLP compliance:
no
Other quality assurance:
other: ISO 3104
Type of method:
capillary viscometer (static)
Remarks:
Micro-Ubbelohde viscometer according to DIN 51 562
Standard covering the apparatus used:
Water bath and thermostat (Lauda)
Thermostat Type E200
Circulating cooler DL K 10
Calibrated thermometer
Micro-Ubbelohde viscometer
Timing device Schott AVS
Specific details on test material used for the study:
- Name of test material (as cited in study report): 2-Hydroxyethyl methacrylate
- Physical state: liquid
- Analytical purity: 98.9%
- Lot/batch No.: 1035092208
- Stability under test conditions: stable
- Storage condition of test material: between room temperature and 4 °C
Key result
Temp.:
20°C
Parameter:
kinematic viscosity (in mm²/s)
Value:
6.36
Key result
Temp.:
40°C
Parameter:
kinematic viscosity (in mm²/s)
Value:
3.42
Conclusions:
The kinematic viscosity of 2-hydroxyethyl methacrylate was measured with a micro-Ubbelohde viscometer according to DIN 51 562 at 20°C and 40°C. Kinematic viscosity at was 6.36 mm²/s at 20 °C and  3.42 mm²/s at 40°C.
Executive summary:

The kinematic viscosity of 2-hydroxyethyl methacrylate was measured with a micro-Ubbelohde viscometer according to DIN 51 562 at 20°C and 40°C. Kinematic viscosity at was 6.36 mm²/s at 20 °C and  3.42 mm²/s at 40°C.

Description of key information

The kinematic viscosity of 2-hydroxyethyl methacrylate was measured with a micro-Ubbelohde viscometer according to DIN 51 562 at 20°C and 40°C. Kinematic viscosity was 6.36 mm²/s at 20 °C and  3.42 mm²/s at 40°C.

Key value for chemical safety assessment

Viscosity:
6.36 mm²/s (static)
at the temperature of:
20 °C

Additional information