Endpoint:
flammability
Type of information:
experimental study
Adequacy of study:
key study
Reliability:
1 (reliable without restriction)
Rationale for reliability incl. deficiencies:
comparable to guideline study
Justification for type of information:
Experimental test result performed using standard test guidelines
Qualifier:
according to
Guideline:
other: It is how easily substance can burn or ignite, causing fire or combustion by brief contact with an ignition source.
Principles of method if other than guideline:
It is how easily substance can burn or ignite, causing fire or combustion by brief contact with an ignition source
GLP compliance:
not specified
Specific details on test material used for the study:
- Name of test material: Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched
- Molecular formula: C17 H28 O2
- InChI=1S/C17H28O2/c1-2-3-4-5-6-7-8-9-16-10-12-17(13-11-16)19-15-14-18/h10-13,18H,2-9,14-15H2,1H3
- Substance type: Organic
- Physical state: Liquid
Remarks on result:
other: Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched not ignited when the flame of bunsen burner having temperature of approximately 950°C was brought in contact with it.
Interpretation of results:
other: non flammable
Conclusions:
Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched does not indicate any ignition when the flame of bunsen burner having temperature of approximately 950°C is brought in contact with it. Thus it can be concluded that Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched is not flammable at high temperature. However since such high temperatures are not found under normal circumstances of transportation and use, thus Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched was considered non-flammable for chemical safety assessment.
Executive summary:

Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched does not indicate any ignition when the flame of bunsen burner having temperature of approximately 950°C is brought in contact with it. Thus it can be concluded that Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched is not flammable at high temperature. However since such high temperatures are not found under normal circumstances of transportation and use, thus Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched was considered non-flammable for chemical safety assessment.

Description of key information

Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched does not indicate any ignition when the flame of bunsen burner having temperature of approximately 950°C is brought in contact with it. Thus it can be concluded that Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched is not flammable at high temperature. However since such high temperatures are not found under normal circumstances of transportation and use, thus Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched was considered non-flammable for chemical safety assessment.

Key value for chemical safety assessment

Additional information

Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched does not indicate any ignition when the flame of bunsen burner having temperature of approximately 950°C is brought in contact with it. Thus it can be concluded that Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched is not flammable at high temperature. However since such high temperatures are not found under normal circumstances of transportation and use, thus Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched was considered non-flammable for chemical safety assessment.

Justification for classification or non-classification

Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched does not indicate any ignition when the flame of bunsen burner having temperature of approximately 950°C is brought in contact with it. Thus it can be concluded that Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched is not flammable at high temperature. However since such high temperatures are not found under normal circumstances of transportation and use, thus Poly (oxy-1,2-ethanediyl), alpha-(4-nonylphenyl)-omega-hydroxy-, branched was considered non-flammable for chemical safety assessment.