The result of specific surface area were as follows:
Mass of dried cell (g): 10.4974
Mass of dried cell and test item after degassed (g): 10.9096
Mass of degassed test item (g): 0.4122
C constant: 64.5047
Specific surface area of test item (m²/g): 15
Specific surface area of the fibre in batch No. 15-11-519 was
determined to be 15 m²/g.
The average of fibre length, diameter and aspect ratio
(length/diameter) of the fibre in the test item (Batch No. 15-11-519) is
shown in the following table:
Average of aspect ratio
The fibres from 5 production batches, including batch No.
15-11-519, were also observed by SEM. The average and standard deviation
of fibre length, diameter and aspect ratio are shown in the following
Average of 5 batches
Two hundreds of fibre for batch No. 15-11-519 is measured for its
length and diameter. The range and average of fibre length of batch No.
15-11-519 were 1.8 - 20 µm and 5.2 µm, respectively. The range and
average of fibre diameter were 48 - 372 nm and 148 nm, respectively.
18.5 % of the particles had a diameter ≤100 nm. The average of the
aspect ratio was 35.
The average of 5 production batches for average fibre length,
average fibre diameter and average of aspect ratio were 4.3 µm, 150 nm
and 29, respectively. In the 5 batches the percentage of particles ≤100
nm ranged from 8.0 % to 21.5 % (13.6 % average).
Information on Registered Substances comes from registration dossiers which have been assigned a registration number. The assignment of a registration number does however not guarantee that the information in the dossier is correct or that the dossier is compliant with Regulation (EC) No 1907/2006 (the REACH Regulation). This information has not been reviewed or verified by the Agency or any other authority. The content is subject to change without prior notice.Reproduction or further distribution of this information may be subject to copyright protection. Use of the information without obtaining the permission from the owner(s) of the respective information might violate the rights of the owner.
Welcome to the ECHA website. This site is not fully supported in Internet Explorer 7 (and earlier versions). Please upgrade your Internet Explorer to a newer version.
Do not show this message again