Registration Dossier

Administrative data

Endpoint:
melting point/freezing point
Type of information:
experimental study
Adequacy of study:
key study
Study period:
05 Dec 2017 - 09 Jan 2018
Reliability:
1 (reliable without restriction)
Rationale for reliability incl. deficiencies:
guideline study

Data source

Reference
Reference Type:
study report
Title:
Unnamed
Year:
2018
Report Date:
2018

Materials and methods

Test guidelineopen allclose all
Qualifier:
according to
Guideline:
EU Method A.1 (Melting / Freezing Temperature)
Version / remarks:
2016
Deviations:
no
Qualifier:
according to
Guideline:
OECD Guideline 102 (Melting point / Melting Range)
Version / remarks:
1995
Deviations:
no
Qualifier:
according to
Guideline:
EPA OPPTS 830.7200 (Melting Point / Melting Range)
Version / remarks:
1998
Deviations:
no
GLP compliance:
yes
Type of method:
differential scanning calorimetry

Test material

Reference
Name:
Unnamed
Type:
Constituent
Test material form:
solid: particulate/powder
Details on test material:
- Appearance: White powder
- Storage condition of test material: At room temperature

Results and discussion

Melting / freezing point
Key result
Melting / freezing pt.:
138 °C

Any other information on results incl. tables

TGA EXPERIMENT (PRELIMINARY TEST)

Starting at 250°C, the weight of the sample decreased slightly, yet up to 550°C a significant decrease in sample weight was not observed.

After the experiment, a black molten residue remained in the sample container. The change of the colour indicated reaction and/or decomposition of the test item.

DSC EXPERIMENT 1

An endothermic peak was observed between 125°C and 150°C. The extrapolated onset temperature of the peak was 138.001°C. The endothermic effect was most likely caused by melting of the test item. An endothermic peak followed by an exothermic peak was observed between 225°C and 400°C. The effects were ascribed to reaction and/or decomposition of the test item.

After the experiment, a brown molten residue remained in the sample container. The change of the colour indicated reaction and/or decomposition of the test item. Based on this visual observation, it was concluded that the test item had molten and that the change of the colour demonstrated reaction and/or decomposition of the test item.

DSC EXPERIMENT 2

In order to investigate the melting peak, in Experiment 2 heating was stopped directly after the melting peak.

The extrapolated onset temperature was 138.011°C. After the experiment, a colourless molten residue remained in the sample container. It demonstrated that melting was the reason for the endothermic effect.

DATA HANDLING

The melting temperature was determined as the mean extrapolated onset temperature of Experiment 1 and Experiment 2.

Applicant's summary and conclusion

Conclusions:
The melting temperature of the substance was determined to be 138.0°C.
Executive summary:

Differential Scanning Calorimetry (DSC) experiments were performed in a GLP study according to EC A.1, OECD 102 and OPPTS 830.7200.

The melting temperature of the substance was determined in duplicate obtaining a mean value of 138.0°C.